This article reports research results related to bioactivity and cytotoxicity tests using neutral red uptake method for glass powders and bulk glass ceramics belonging to the SNCP (SiO2-Na2O-CaO-P2O5) system. The obtained materials showed bioactivity when immersed in SBF promoting the surface deposition of HAp. When analyzed as powders, cytotoxicity was evidenced in the processed materials but not when bulk samples were tested.

Glass-ceramics foams prepared from glasses of the SiO2-Na2O-CaO-P2O5 by replication process were obtained and characterized in terms of their chemical and physical properties by X-ray fluorescence, X-ray diffraction, laser diffraction, thermal analysis, density, mechanical strength, microstructural and cytotoxic analysis. The results showed that it is possible to produce glass-ceramic foams by the replication method with optimized properties but cytotoxic analysis indicates that the glass-ceramic foams are not bioactive materials. Mechanical strength values varying from 0.5 to 1.0 MPa and from 0.8 to 2.3 MPa were reached for mean particle sizes of 10 and 6 µm, respectively.